玉米苞叶组织细胞结构生物质碳的制备及显微结构的研究
周晓亮,马 林*,杨一君,余 宇,张致远,罗 马,曾祥昇,严铮洸
(1.北京交通大学物理科学与工程学院,北京100044;2. 北京工业大学材料学部,北京100124)
摘 要 采用一步热解法,使用常见的玉米果穗苞叶为原料,制备了保留玉米苞叶组织细胞结构的生物质碳膜,采用扫描电镜,透射电镜等技术手段对样品的形貌和结构进行了表征,样品表面有明显的维管束以及大量的气孔的存在。本工作在生物质废弃物利用,以及储能材料开发等方面有参考价值。
关键词 生物质;细胞结构;电子显微学;储能
中图分类号:TM911;Q246;TG115.21+5.3;S216 文献标识码:A doi:10.3969/j.issn.1000-6281.2024.03.010
Preparation, microstructure, and energy storage performance of biomass carbon from corn bract
ZHOU Xiaoliang1, MA Lin2*, YANG Yijun1, YU Yu1, ZHANG Zhiyuan1, LUO Ma1, ZENG Xiangsheng1, YAN Zhengguang2
(1. School of physical science and engineering, Beijing Jiaotong university, Beijing 100044; 2 Faculty of materials and manufacturing, Beijing university of technology, Beijing 100124, China)
Abstract One-pot pyrolysis method was utilized to fabricate biochar membranes with cell structures from corn bracts. SEM and TEM techniques were used to study the microstructure and morphology of samples. Leaf veins and stomata were observed in these samples. Biochar membranes were used as working electrodes without any binder or conductive additives, a reversible specific capacity of 218 mAh/g was maintained after 200 cycles at a current density of 100 mA/g. This work provides a reference for the utilization of biomass waste and the development of energy storage materials.
Keywords biomass; cell structure; electron microscopy; energy storage
“全文下载请到同方知网,万方数据库或重庆维普等数据库中下载!”
[1] 李强. 生物质基纳米孔碳电极材料的制备及其超级电容性能的研究[D]. 淄博:山东理工大学化学化工学院,2019:2-4.
[2] MARINO C, CABANERO J, POVIA M,et al. Biowaste lignin-based carbonaceous materials as anodes for Na-ion batteries[J]. J Electrochem Soc, 2018, 165: A1400-A1408.
[3] RYBARCZYK M K, LI Y, QIAO M, et al. Hard carbon derived from rice husk as low cost negative electrodes in Na-ion batteries[J]. J Energy Chem, 2019, 29: 17–22
[4] SAHA A, SHARABANI T, EVENSTEIN E, et al. Probing electrochemical behaviour of lignocellulosic, orange peel derived hard carbon as anode for sodium ion battery[J]. J Electrochem Soc, 2020, 167: 090505.
[5] NIU Q, GAO K, TANG Q, et al. Large-size graphene-like porous carbon nanosheets with controllable N-doped surface derived from sugarcane bagasse pith/chitosan for high performance supercapacitors[J]. Carbon, 2017, 123: 290-298.
[6] SEO S, CHOI C, KIM B K, et al. Fabrication of highly porous carbon as sulfur hosts using waste green tea bag powder for lithium–sulfur batteries[J]. Ceram Int, 2017, 43: 2836-2841.
[7] CONDER J, VAULOT C, MARINO C, et al. Chitin and chitosan-structurally related precursors of dissimilar hard carbons for Na-ion battery[J]. ACS Appl Energy Mater, 2019, 2: 4841−4852.
[8] YOON D, HWANG J, CHANG W, et al. Carbon with expanded and well-developed graphene planes derived directly from condensed lignin as a high-performance anode for sodium-ion batteries[J]. ACS Appl Mater Interfaces, 2018, 10: 569-581.
[9] LI Q, WU X, ZHAO Y, et al. Nitrogen-doped hierarchical porous carbon through one-step activation of bean curd for high-performance supercapacitor electrode[J]. Chem Electro Chem, 2018, 5: 1606-1614.
[10] LI H, SHEN F, LU W, et al. Carbonized leaf membrane with anisotropic surfaces for sodium ion battery[J]. ACS Appl Mater Interfaces, 2016, 8: 2204-2210.
[11] WOOD A R, GARG R, JUSTUS K, et al. Intact mangrove root electrodes for desalination [J]. RSC Adv, 2019, 9: 4735–4743.
[12] YU X, WANG Y, LI L, et al. Soft and wrinkled carbon membranes derived from petals for flexible supercapacitors[J]. Scientific Reports, 2017, 7: 45378.
[13] 于川茗,李林,蔡毅超,扫描电镜在电池材料领域的应用[J]. 电子显微学报,2021,40(3):339-347
[14] 李淑瑜,周晓亮,马林,等. 锂离子电池电极材料LiTi2(PO4)3的纤维模板法制备、微结构和电化学性能研究[J]. 电子显微学报,2015,34(5):382-387